Corrosion mechanism of cement-bonded Al2O3–MgAl2O4 pre-cast castables in contact with molten steel and slag

In this work, a cement-bonded corundum-spinel (Al₂O₃–MgAl₂O₄) pre-cast refractory brick with two typical Al₂O₃ aggregates was designed as the refractory lining. Corroded microstructure of the used corundum-spinel bricks after industrial trials in a commercial RH refining ladle was analyzed. Degradation processes of two types of alumina aggregates in the same corroded interface also were discussed. Typical corroded microstructure revealed that needle-like calcium hexaaluminate (CA₆) was observed in the matrix of the original layer. The formation of CA₆ was attributed to the reactions with pure calcium aluminate cement and matrix components under a high-temperature gradient during refining. Furthermore, the corrosion process of the used Al₂O₃–MgAl₂O₄ bricks would be discussed based on a post-mortem microstructural characterization, and the corrosion mechanism of the two types of aggregates was also elucidated.     

热轧圆钢热顶锻裂纹原因分析

热顶锻合格率是反映热轧圆钢实物质量的一个重要指标。在对国内外热轧圆钢热顶锻质量控制研究成果综述的基础上，对热轧圆钢的热顶锻质量进行了全面的调查、统计和试验研究，归纳了引起热轧圆钢热顶锻裂纹的常见原因，介绍了热顶锻裂纹分析步骤。通过对热顶锻裂纹的形貌和金相组织进行分析，阐述了引起热顶锻裂纹的冶炼因素和轧制因素，并进行了举例说明。     

中国抗中子辐照钢的抗辐照设计与验证

聚变堆等未来先进核能系统要求材料在强流高能中子辐照下长期保持良好的结构稳定性和机械性能。为适应未来先进核能技术发展的需要，中国科学院核能安全技术研究所•凤麟团队牵头研发了具有我国自主知识产权的中国抗中子辐照钢--CLAM钢。CLAM钢的设计考虑了未来核能清洁性的要求，以及苛刻服役环境中材料抗辐照、耐高温、耐腐蚀等性能要求。通过中子学计算分析设计了低活化成分范围，基于选择性纳米相析出进行了抗辐照、耐高温性能优化设计。针对材料的抗辐照性能，利用国内外中子、离子、电子及等离子体辐照设施开展了系列辐照考验研究，通过多角度表征辐照前后材料的微观结构和宏观性能，综合评估了材料的辐照性能，并与国际上同类材料在相近或相同条件下的辐照性能进行了对比分析，结果表明CLAM钢具有良好的抗辐照性能。     

中国钢铁产品全生命周期评价理论与实践

阐述了全生命周期评价的基本原理和内涵，分析了全生命周期评价在国内外钢铁行业的应用现状、差距及研究进展情况，论述了钢铁企业开展全生命周期评价的重要意义，研究了中国政府、行业协会、钢铁企业、咨询机构等在推进绿色设计产品评价技术规范系列标准等方面开展的相关工作。提出钢铁行业全生命周期评价推广与应用的具体建议，探讨了发展方向，对钢铁企业开展生命周期评价具有一定的指导意义。     

Synergistic interaction of 2-amino 4-methyl benzothiazole (AMBT) and benzotriazole (BTZ) offers excellent protection to mild steel exposed in acid atmosphere at elevated temperatures: Electrochemical,computational and surface studies

The synergistic interactions and corrosion protection properties of 2-amino 4-methyl benzothiazole, (AMBT) and 1, 2, 3-benzotriazole (BTZ) have been studied for mild steel in HCl at elevated temperatures. The extent of synergistic interaction increases with temperature. The methods of study include the conventional weight loss studies, computational screening, surface characterization and electrochemical studies. Quantum chemical approach was used to calculate some electronic properties of the molecules and to ascertain the synergistic interaction, inhibitive effect and molecular structures. The corrosion inhibition efficiencies and the global chemical reactivity relate to parameters like total energy, E_HOMO, E_LUMO and gap energy (ΔE). Condensed atom Fukui functions also calculated using DFT at B3LYP/6-31G* level, and were found to be correlating with the experimental results.     

深井超深井钻井堵漏材料高温老化性能评价

深井超深井钻进裂缝性油气层极易发生频繁的钻井液漏失,造成严重储层损害和重大经济损失。储层段钻进过程中经常发生重复性漏失,意味着仅用酸溶率、粒度分布等常规堵漏材料评价指标已不能满足钻井液漏失控制工程需要。笔者以塔里木盆地克深气田钻井常用的核桃壳、毫米级碳酸钙为研究对象,开展了堵漏材料高温老化评价实验。实验评价结果表明,在180℃的柴油中老化24 h后,核桃壳的颜色由黄色变成黑色,质量损失率为25.16 % ,摩擦系数下降28.24 % ,抗压强度下降21.21 % ;毫米级碳酸钙的颜色由白色变成淡黄色,质量损失率为2.47 % ,摩擦系数下降1.33 % ,抗压强度基本不变;由高温老化后的核桃壳和毫米级碳酸钙所形成的封堵层,其承压能力下降了48.84 % 。分析指出,堵漏材料高温老化失效是深井超深井裂缝封堵层结构破坏并在储层段发生重复性漏失的一个重要因素。     

Ms以下温度等温淬火对中碳贝氏体钢相变和性能影响

摘要：设计了马氏体起始相变温度（Ms）以上和以下2个不同温度等温淬火试验，结合热膨胀仪、扫描电镜显微组织、X光衍射和拉伸试验等试验手段，研究了对比于Ms以上温度等温淬火试验，Ms以下等温淬火对中碳贝氏体钢相变、组织和性能的影响。结果表明，贝氏体相变可以发生在Ms温度以下，且其相变动力学被明显促进。相比于Ms以上温度等温淬火，Ms温度以下等温淬火虽然可以加速相变动力学，但导致强度和伸长率下降，因此降低了最终的力学性能。这主要是因为Ms温度以下等温淬火试样组织内部出现了大量的回火无热马氏体（AM）和少量的贝氏体和残余奥氏体（RA）。因此，Ms温度以下等温淬火热处理后的组织性能未必优于Ms温度以上等温处理后组织性能，这主要取决于具体的成分和工艺。